导致高压击穿现象的原因

分享到:
 发布时间: 2014-11-19点击:

导致高压击穿现象的原因:

1、电源不匹配或使用不同规格的电源工作(使用高功率的电源激发低功率的管子)。超过激光管所能承受的额定电压,导致激光管的破损。

2、水冷条件不好,冷却水没有充满整个水冷管有气泡存在,在没有水冷的位置,局部温度过高,导致玻璃料性变化造成激光管玻璃局部的破损。

3、玻璃材料生产时温度、原料、工艺等原因的影响造成玻璃材料内有微小气泡或厚度的不均匀,出现此种情况在高压放电的情况下造成薄弱位置的破损。

 

What cause CO2 laser tube high-voltage breakdown

1. The power supply does not match (power supply specifications not meet the requirements of the laser tube). For example,using high-power supply coordinated with low-  power tube. The voltage exceed the rated voltage of co2 laser tube, resulting in damage.

2. Poor water cooling conditions. There are bubbles in built-in loop cooling water tube, partial no cooling water protection, resulting in high temperature, causing damage.                       3.There are tiny glass bubbles or uneven thickness. In glass production process, due to temperature, raw materials, technology and other reasons, creating a very small number of such cases occur within the glass material, in the case of high voltage discharge, location of the damage caused by the weak.